2 results
Use of Competitive Ion Exchange for Intercalation of Montmorillonite with Hydroxy-Aluminum Species
- F. Figueras, Z. Klapyta, P. Massiani, Z. Mountassir, D. Tichit, F. Fajula, C. Gueguen, J. Bousquet, A. Auroux
-
- Journal:
- Clays and Clay Minerals / Volume 38 / Issue 3 / June 1990
- Published online by Cambridge University Press:
- 02 April 2024, pp. 257-264
-
- Article
- Export citation
-
Three montmorillonite samples, from Wyoming (particle size <0.2 µm, 4.6 wt. % Fe2O3), Greece (<14 µm, 6.5 wt. % Fe2O3), and Poland (0.5 wt. % Fe2O3, two fractions <2 µm and 2–10 µm) were intercalated with hydroxy-Al species. The amount of hydroxy-Al cations exchanged by the clays depended on the particle size: it decreased from 31 wt. % Al2O3 for 0.2 µm in size to 22.6 wt. % for >2 µm. The X-ray powder diffraction (XRD) pattern showed that most of the material was not intercalated after refluxing at 80°C for 2 hr; several redispersions of the pillared clay in hot water were required to obtain a single sharp XRD line at 18.6 Å. The diffusion of the Al cations therefore limited the cation-exchange process. The addition of NH4+ to the pillaring solution decreased the amount of Al fixed by the clay from 31 (no NH4+ to 26 wt. % (NH4+/Al = 10), but increased slightly the microporous volume of the resulting pillared material from 0.13 to 0.14 ml/g. The competition between NH4+ and Al-hydroxy cations for ion-exchange sites forced the Al species into the interlayer space and increased the homogeneity of the resulting pillared material. The influence of particle size on the amount of Al exchanged was then reduced. After calcination in air at 700°C the pillared Wyoming clay retained a microporous volume of 0.09 ml/g if no NH4+ was added, compared with 0.11 ml/g for a NH4+/Al ratio of 10. The Fe content of the clay affected the thermal stability of pillared clays at 800°C: for two samples prepared by competitive ion exchange (NH4+/Al = 10) the microporous volume increased from 0.06 ml/g for 6.4 wt. % Fe2O3 to 0.08 ml/g for 0.5 wt. % Fe2O3. The acidity of the pillared clay was determined by calorimetric adsorption of ammonia at 150°C, on samples calcined at 500°C. Pillared montmorillonite prepared using noncompetitive intercalation showed a weak acid strength: most sites adsorbed ammonia with an enthalpy of 65 kJ/mole. The intercalation of the same original clay using competitive ion exchange yielded a solid that possessed both weak (heat = 60 kJ/mole) and strong (120 kJ/mole) acid sties. Competitive ion exchange appears to be a simple means of preparation of large quantities of pillared clays of reasonable thermal stability and higher acidity than those obtained by conventional methods.
Sintering of Montomorillonites Pillared by Hydroxy-Aluminum Species
- D. Tichit, F. Fajula, F. Figueras, B. Ducourant, G. Mascherpa, C. Gueguen, J. Bousquet
-
- Journal:
- Clays and Clay Minerals / Volume 36 / Issue 4 / August 1988
- Published online by Cambridge University Press:
- 02 April 2024, pp. 369-375
-
- Article
- Export citation
-
The sintering of montmorillonites pillared by hydroxy-Al species was investigated by several techniques. The change of the microporosity of the pillared interlayer clay with temperature shows that sintering was mainly due to the loss of microporosity. On calcination of the parent clay at 760°C, the X-ray powder diffraction pattern did not change; the 060 line shifted only slightly from 8.988 to 9.017 Å. The infrared (IR) spectrum suggested some dehydroxylation, but the structure appears to have been preserved. On calcination of the pillared clay at >700°C, the intensity of the 001 line decreased steadily, the 060 line broadened, and the b parameter decreased slightly from 8.988 to 8.928 Å. Fe3+ ions apparently occupied only one site after calcination at 300°C and two sites after calcination at 700°C. Smaller isomer shifts and higher quadrupole splittings in the Mössbauer spectra suggest that calcination produced more covalent bonding of Fe3+ and a highly distorted structure. The IR spectrum was significantly modified by calcination of the sample, and the 935- and 1125-cm−1 bands disappeared and the 1035-cm−1 band broadened. These results suggest that at <700°C the pillars sintered and that the clay progressively decomposed at >750°C. The pillaring-induced decrease of thermal stability of the clay was likely due to the introduction of protons during the first step of the preparation. The thermal stability of these Al-pillared interlayer complexes is comparable to that reported for hydroxy-silicoaluminum montmorillonites and fluorhectorites.